Method for sealing a battery case

ABSTRACT

This invention is an improved method for making a battery case feedthrough. It utilizes stainless steel or titanium metal clad with aluminum. The use of the clad metal enables the fabrication of the battery case and cover and feedthrough pin assembly where a high temperature ceramic-metal hermetic seal is needed between a stainless steel feedthrough pin and a ceramic insulator; and between a ceramic insulator and a surrounding hollow cylinder. A high temperature hermetic seal is also used to fasten the feedthrough pin assembly to the upper stainless steel part of the stainless steel-aluminum clad cover. Titanium can be substituted for stainless steel. Lower temperature metal-metal hermetic seals are needed between the aluminum-clad part of the cover and the aluminum battery casing.

FIELD OF THE INVENTION

[0001] This invention relates to battery case feedthroughs. It also relates to clad metals. Also it relates to high temperature ceramic-metal hermetic seals and to lower temperature metal-metal hermetic seals.

BACKGROUND OF THE INVENTION

[0002] There are different methods for forming clad metal, such as a plate of stainless steel clad with aluminum. In one method (U.S. Pat. No. 4,213,558, Hirobe, et al.), sheet metal cladding is fed onto one or both faces of the hot solidified continuously cast strip being withdrawn from the casting means and the assembly is then passed to a hot roll bonding system for cladding. Another method (U.S. Pat. No. 4,966,748, Miyasaka et al.) produces a clad metal by forming a layer of a dissimilar metal powder on the surface of a base metal by cold fixing the powder to the surface under pressure, densing only the surface and a subsurface area of the layer of the dissimilar metal powder by melting and immediately solidifying in a vacuum, compressing the layer of the dissimilar metal powder together with the base metal at a temperature not higher than the solidus-line temperature of the two dissimilar metals under a pressure of not lower than kgf/cm² using a hot isostatic press, and hot working the layer of the dissimilar metal powder together with the base metal.

[0003] Ceramic to stainless steel and ceramic to titanium bonds are particular examples of ceramic to metal bonds. Braze bonding, for example, aluminum oxide and zirconium oxide ceramics to metals, including titanium, stainless steel, molybdenum, tantalum, and cobalt-chromium alloys, can be done using a braze, comprising 30% nickel and 70% titanium (U.S. Provisional Patent Application, Serial No., ______; U.S. patent application, Ser. No. ______). Another example of a braze bond includes the preferred method for joining zirconium oxide containing 3% yttrium to preferably a metal alloy, namely, titanium and niobium (55% Ti and 45% Nb), using the nickel-titanium braze (50% Ni and 50% Ti) (U.S. Provisional Patent Application, Serial. No. ______; U.S. patent application, Ser. No. ______).

[0004] How can a high temperature brazing operation for joining metal and ceramic be made compatible with the further low temperature joining of two metal surfaces, these two metal surfaces having a relatively low melting temperature?

SUMMARY OF THE INVENTION

[0005] This invention makes use of clad metals in order to provide high temperature and low temperature seals. For example, stainless steel and aluminum can form a hermetically bonded clad combination. The stainless steel or titanium can be used with a high temperature braze in order to form a hermetic seal bond with a ceramic material such as aluminum oxide or zirconium oxide.

[0006] The method of use of this for battery feedthroughs is the placement of a stainless steel or titanium pin through a cylinder of ceramic, such as aluminum oxide or zirconium oxide. This ceramic is surrounded by on annular cylinder of stainless steel or titanium. A hole is formed in an aluminum clad stainless-steel sheet, with the stainless steel forming the upper layer. A high temperature welding process, for example, hermetically bonds the upper stainless-steel layer to the outer stainless steel cylinder of the feedthrough assembly. The lower aluminum layer is easily laser welded to the battery case cover of aluminum. If the clad metal was not used, the high temperature used to embed the central stainless-steel feedthrough pin in the ceramic cylinder, would destroy the aluminum battery casing and cover.

BRIEF DESCRIPTION OF THE DRAWINGS

[0007] The above and other features and advantages of the invention will be more apparent from the following detailed description wherein:

[0008]FIG. 1 shows an exploded view of the feedthrough for the battery casing with aluminum clad stainless steel (or titanium) material;

[0009]FIG. 2 shows a non-exploded view of FIG. 2.

DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENT

[0010] The following description is of the best mode presently contemplated for carrying out the invention. This description is not to be taken in a limiting sense, but is merely made for the purpose of describing the general principles of the invention. The scope of the invention should be determined with reference to the claims.

[0011] This invention makes use of clad metals in order to provide high temperature and low temperature seals. For example, stainless steel, and titanium, can form an hermetically bonded clad combination with aluminum. The stainless steel or titanium can be used with a high temperature braze in order to form a hermetic seal bond with a ceramic material such as aluminum oxide or zirconium oxide. The method of use of this for battery feedthroughs is that of the baking in, or brazing in, of a stainless steel or titanium pin (1) in a cylinder of ceramic (2), such as aluminum oxide or zirconium oxide. This ceramic is surrounded by on annular cylinder (3) of stainless steel or titanium. The cylindrical combination of metal feedthrough pin, ceramic insulator, and metal surrounding cylinder allows for welding the stainless steel, or titanium, outer cylinder, hermetically, to the upper part of a stainless steel, or titanium, sheet (4), aluminum clad (5), with a hole (6) prepared in it. The upper part of said clad sheet is stainless steel (or titanium) (4), the lower part is aluminum (5), and the lower sheet can be hermetically welded to an aluminum case (7), for example, an aluminum battery case.

[0012] If the clad metal were not used, the high temperature used to hermetically bond the feedthrough pin assembly (stainless-steel feedthrough pin, ceramic cylinder, outer stainless-steel cylinder) would require a stainless steel cover with which to bond the assembly. However, in trying to bond the stainless-steel cover to the aluminum case, the welding, or brazing, temperature would melt the aluminum. The melting point temperatures of the metals are aluminum 660.37° C., stainless steel-303, 1427° C., and titanium 1660+/−10° C. In FIG. 2, Low temperature hermetic welds are shown at (11) and (12). High temperature welds are shown at (13) and (14)

[0013] While the invention herein disclosed has been described by means of specific embodiments and applications thereof, numerous modifications and variations could be made thereto by those skilled in the art without departing from the scope of the invention set forth in the claims. 

What is claimed is:
 1. A method for bonding high melting point and low melting point substances comprising the steps of: a. joining the high temperature substances one-to-one; b. cladding a low melting point substance to a part of the high melting point substance wherein said low melting point cladding substance is slightly distant from the high temperature joining point; c. attaching the low melting point cladding to a similar low melting point substance.
 2. The method as in claim 1 further comprising the steps of: a. utilizing a ceramic for one of the high melting point substances; b. utilizing a metal for the other high melting point substance; c. utilizing a different metal for the low melting point substance.
 3. The method as in claim 2 further comprising the step of forming the low melting point metal from aluminum.
 4. The method as in claim 3 further comprising the step of forming the ceramic component from aluminum oxide.
 5. The method as in claim 3 further comprising the step of forming the ceramic component from zirconium oxide.
 6. The method as in claim 4 or in claim 5 further comprising the step of forming the high melting point metal from stainless steel.
 7. The method as in claim 4 or in claim 5 further comprising the step of forming the high melting point metal from titanium.
 8. An apparatus wherein high melting point and low melting point substances are bonded together further comprising a. two high temperature substances joined one-to-one; b. a low melting point substance clad to a part of the high melting point substance wherein said low melting point cladding substance is slightly distant from the high temperature joining point; c. said low melting point cladding attached to a similar low melting point substance.
 9. The apparatus as in claim 8 comprising: a. a ceramic utilized for one of the high melting point substances; b. a metal utilized for the other high melting point substance; c. a different metal utilized for the low melting point substance.
 10. The apparatus as in claim 9 comprising the low melting point metal formed from aluminum.
 11. The apparatus as in claim 10 comprising the ceramic component formed from aluminum oxide.
 12. The apparatus as in claim 10 comprising the ceramic component formed from zirconium oxide.
 13. The apparatus as in claim 11 or in claim 12 comprising the high melting point metal formed from stainless steel.
 14. The apparatus as in claim 11 or in claim 12 comprising the high melting point metal formed from titanium.
 15. A battery feedthrough comprising a center conducting pin made from a metal selected from the group-consisting of stainless steel and titanium; an electrical insulator made from a ceramic selected from the group consisting of aluminum oxide and zirconium oxide; said pin and said ceramic surrounded by a hollow cylinder of a metal selected from the group consisting of stainless steel and titanium; wherein said pin, said ceramic, and said surrounding metal hollow cylinder form a feedthrough-pin assembly; said feedthrough-pin assembly fitted through a hole in a clad metal cover slightly larger than the feedthrough-pin assembly; said clad metal being aluminum on the side facing toward a cylindrical aluminum battery casing; said upper clad surface being the same metal selected for the outer metal cylinder of the feedthrough-pin assembly.
 16. The battery feedthrough as in claim 15 wherein the lower aluminum part of the clad cover does not meet the feedthrough-pin assembly.
 17. The battery feedthrough as in claim 16 wherein the upper clad surface, which is a metal selected from the group consisting of stainless steel and titanium, is welded to the outer cylinder of the feedthrough-pin assembly.
 18. The battery feedthrough as in claim 17 wherein the upper stainless steel or titanium part of the clad cover-to-outer cylinder of feedthrough-pin assembly weld is hermetic.
 19. The battery feedthrough as in claim 18 wherein the lower aluminum part of the clad cover is welded to the aluminum battery casing.
 20. The battery feedthrough as in claim 19 wherein the lower aluminum part of the clad cover is welded to the aluminum battery casing.
 21. The battery feedthrough as in claim 20 wherein the lower aluminum part of the clad cover-aluminum battery casing weld is hermetic. 